Photocatalytic and Photo-Fenton Catalytic Degradation Activities of Z-Scheme Ag2S/BiFeO3 Heterojunction Composites under Visible-Light Irradiation
摘要： Z-scheme Ag2S/BiFeO3 heterojunction composites were successfully prepared through a precipitation method. The morphology and microstructure characterization demonstrate that Ag2S nanoparticles (30–50 nm) are well-decorated on the surfaces of polyhedral BiFeO3 particles (500–800 nm) to form Ag2S/BiFeO3 heterojunctions. The photocatalytic and photo-Fenton catalytic activities of the as-derived Ag2S/BiFeO3 heterojunction composites were evaluated by the degradation of methyl orange (MO) under visible-light irradiation. The photocatalytic result indicates that the Ag2S/BiFeO3 composites exhibit much improved photocatalytic activities when compared with bare Ag2S and BiFeO3. The optimum composite sample was observed to be 15% Ag2S/BiFeO3 with an Ag2S mass fraction of 15%. Furthermore, the addition of H2O2 can further enhance the dye degradation efficiency, which is due to the synergistic effects of photo- and Fenton catalysis. The results of photoelectrochemical and photoluminescence measurements suggest a greater separation of the photoexcited electron/hole pairs in the Ag2S/BiFeO3 composites. According to the active species trapping experiments, the photocatalytic and photo-Fenton catalytic mechanisms of the Ag2S/BiFeO3 composites were proposed and discussed.
关键词： polyhedral BiFeO3 particles,photo-Fenton catalysis,Ag2S nanoparticles,photocatalysis,Z-scheme Ag2S/BiFeO3 heterojunction
更新于2025-11-19 16:46:39
-
Direct Observation of Curved Surface Enhanced Disordering in Ag <sub/>2</sub> S Nanoparticles
摘要： Surface induced order-disorder phase transition has been widely studied on flat bulk surfaces, while such a transition is poorly understood on curved surfaces in nanoscale. Here, we report a direct observation of the dynamic behaviors of surface-initiated disordering in Ag2S nanoparticles using atomic resolution in-situ transmission electron microscopy. It was found that the disordering behavior is different from the traditional model that the disordered layer follows a logarithmical thickness dependence with temperature. In particular, the disordering is largely enhanced at higher temperature when the radius of the residual order phase is getting smaller. Moreover, the correlation length of disordered phase was found to be several times larger than the typical value for bulk surfaces. This significantly enhanced disordering in nanoparticles could be attributed to the extra driving force provided by the decreasing of order-disorder interface area.
关键词： nanoscale,Ag2S nanoparticles,in-situ TEM,phase transition,surface-initiated disordering
更新于2025-09-04 15:30:14