All-solution-processed UV-IR broadband trilayer photodetectors with CsPbBr3 colloidal nanocrystals as carriers-extracting layer

摘要： Colloidal quantum dots (CQDs) are very promising nanomaterials for optoelectronics due to their tunable bandgap and quantum confinement effect. Especially, all-inorganic CsPbX3 (X=Br, Cl and I) perovskite nanocrystals (NCs) have attracted enormous interests owing to their promising and exciting applications in photovoltaic devices. In this paper, all-solution-processed broadband photodetectors ITO/ZnO/CsPbBr3/PbS/Au with high-performance were presented. The role of CsPbBr3 QDs layer as the carriers-extracting layer in the trilayer devices was discussed. As compared with bilayer device ITO/ZnO/PbS/Au, both the dark currents and photocurrents under illumination from UV-IR broadband trilayer photodetector ITO/ZnO(80nm)/PbS(150nm)/CsPbBr3(50nm)/Au are enhanced, but the trilayer photodetector ITO/ZnO(80nm)/CsPbBr3(50nm)/PbS(150nm)/Au showed a maximum specific detectivity (D*) of 1.73×1012 Jones with a responsivity (R) of 5.31 A/W under 6.8 mW/cm2 405 nm illumination. However, another trilayer photodetector ITO/ZnO(80nm)/PbS(150nm)/CsPbBr3(50nm)/Au showed a maximum D* of 8.3×1012 Jones with a R of 35 A/W under 1.6 mW/cm2 980 nm illumination. Further, the underlying mechanism for the enhanced performance of trilayer photodetectors was discussed. Thus, this strategy of all-solution-processed heterojunction configuration paves a facile way for broadband photodetectors with high-performance.