Thermally-stable large strain in Bi(Mn0.5Ti0.5)O3 modified 0.8Bi0.5Na0.5TiO3-0.2Bi0.5K0.5TiO3 ceramics
摘要： A N U S C RIP T (1-x)[0.8Bi0.5Na0.5TiO3-0.2Bi0.5K0.5TiO3]-xBi(Mn0.5Ti0.5)O3 (x = 0 ~ 0.06, BNKMT100x) lead-free ferroelectric ceramics were prepared via solid state reaction method. Bi(Mn0.5Ti0.5)O3 induces a structure transition from rhombohedral-tetragonal morphotropic phases to pseudo-cubic phase. Moreover, the wide range of compositions within x = 0.03 ~ 0.055 exhibit large strain of 0.31% ~ 0.41% and electrostrictive coefficient of 0.027 ~ 0.041 m4/C2. Especially, at x = 0.04, the large strain and electrostrictive coefficient are nearly temperature-independent in the range of 25 ~ 100 °C. The impedance analysis shows the large strain and electrostrictive coefficient originate from polar nanoregions response due to the addition of Bi(Mn0.5Ti0.5)O3.
关键词： large strain,thermal stability,composition-insensitivity,lead-free,electric property
更新于2025-09-23 15:23:52
-
Self‐Healable Black Phosphorus Photodetectors
摘要： Large‐strain multilayer actuators (MLAs) were fabricated by tape‐casting 0.91(Na1/2Bi1/2)TiO3–0.06BaTiO3–0.03AgNbO3 (NBT‐BT–3AN) lead‐free incipient piezoceramics co‐fired with Pt inner electrodes. Microstructures, dielectric properties, unipolar and bipolar strain, as well as fatigue properties of the MLAs were investigated. It was found that the actuator consisting of 15 ceramic layers with individual thicknesses of 114 μm could output a large unipolar strain of 0.3% and a dynamic displacement of 5 μm at 6 kV/mm at room temperature. It exhibited excellent cycling stability and provided a high strain of 0.23% after 107 cycles at 6 kV/mm. Moreover, these MLAs still can deliver a strain of 0.20% at 125°C.
关键词： lead‐free piezoceramics,multilayer actuators,large strain,cycling stability,temperature stability
更新于2025-09-11 14:15:04