  • Ultraviolet photodetectors based on doped ZnO films

    摘要： In this paper, we report the realization of ultraviolet (UV) photodetector based on doped ZnO films. The ZnO p-n junction was fabricated on indium tin oxide (ITO) coated glass, which consists of n-type and p-type layers based on Ga-doped (2 at.%) and N-doped (20 at.%) ZnO films, respectively. The current-voltage (IV) characteristics, photosensitivity, photoresponsitivity, and photocurrent gain were derived to determine the performance of the device. At 5 V reverse bias, the ZnO-based UV photodetector exhibits photosensitivity of 10.9, photoresponsivity of 2.1 × 10-2 AW-1, and photoconductive gain of 7.2 × 10-2.

    关键词： ultraviolet photodetectors,sol-gel spin coating,p-n junction,doped ZnO films

    更新于2025-09-12 10:27:22

  • PH SENSITIVITY DEPENDENCY ON THE ANNEALING TEMPERATURE OF SPIN-COATED TITANIUM DIOXIDE THIN FILMS

    摘要： Titanium dioxide (TiO2) thin films were fabricated on indium tin oxide (ITO) glass substrates using the spin coating technique and further were implemented as sensing membranes of the extended gate field effect transistor (EGFET) based pH sensor. The as-deposited thin films were annealed at different temperatures from 200 - 600 °C in room ambient for 20 min. The effects of different annealing temperatures on electrical and crystalline properties were analyzed by I-V two point probes measurement and X-ray diffraction respectively. Meanwhile, the surface morphology of thin films was observed by field emission scanning electron microscope (FESEM). We then measured the transfer characteristics (ID-VG) of the TiO2/ITO sensing membrane using a semiconductor parametric device analyzer for sensor characterization. It was found that, TiO2/ITO sensing membrane annealed at 300 °C achieved higher sensitivity and good linearity of 51.48 mV/pH and 0.99415, respectively in the pH buffer solutions of 4, 7, 10, and 12. Thin film annealed at 300 °C gives higher conductivity thin film of 384.62 S/m. We found that the conductivity of TiO2/ITO thin films was proportional with the sensitivity of sensing membrane.

    关键词： titanium dioxide,Annealing temperature,sol-gel spin coating,extended gate field effect transistor

    更新于2025-09-04 15:30:14