Effects of Substrate Preheating Temperatures on the Microstructure, Properties, and Residual Stress of 12CrNi2 Prepared by Laser Cladding Deposition Technique
摘要： The 12CrNi2 alloy steel powder studied in the present paper is mainly used to manufacture camshafts for nuclear power emergency diesel engines. Laser cladding deposition is of great signi?cance for the manufacture of nuclear power emergency diesel camshafts, which has the advantages of reducing material cost and shortening the manufacturing cycle. However, due to the extremely uneven heating of the components during the deposition process, a complex residual stress ?eld occurs, resulting in crack defects and residual deformation of the components. In the present paper, 12CrNi2 bulk specimens were prepared on the Q460E high-strength structural steel substrate at different preheating temperatures by laser cladding deposition technique, and a ?nite element residual stress analysis model was established to investigate the effects of different preheating temperatures on the microstructure, properties, and residual stress of the specimens. The results of the experiments and ?nite element simulations show that with the increase of preheating temperature, the content of martensite/bainite in the deposited layer decreases, and the ferrite content increases. The proper preheating temperature (150 ?C) has good mechanical properties. The residual stress on the surface of each specimen decreases with the increase of the preheating temperature. The longitudinal stress is greater at the rear-end deposition part, and the lateral residual stress is greater on both sides along the scanning direction.
关键词： substrate preheating,12CrNi2 alloy steel powder,residual stress,laser cladding deposition,microstructure and properties
更新于2025-11-28 14:24:20
-
Numerical Study on Thermodynamic Behavior during Selective Laser Melting of 24CrNiMo Alloy Steel
摘要： In this paper, a multi-layer and multi-track ?nite element model of 24CrNiMo alloy steel by selective laser melting (SLM) is established by using the ABAQUS software. The distribution and evolution of temperature ?eld and stress ?eld and the in?uence of process parameters on them are systematically studied. The results show that the peak temperature increases from 2153 C and the residual stress increases from 335 MPa to 364 MPa with increasing laser power from 200 W to 300 W; the peak temperature decreases from 2905 C and the residual stress increases from 327 MPa to 363 MPa with increasing scanning speed from 150 mm/s to 250 mm/s; the peak C and the residual stress decreases from 354 MPa to 300 temperature increases from 2621 MPa with increasing preheating temperature from 25 C. Far away from scanning area, far away from starting point, and the adjacent areas with vertical scanning direction, resulting in a uniform temperature distribution, help to reduce the residual stress. Due to the remelting e?ect, the interlayer scanning angle changing helps to release the residual stress of the former layer causing a smaller residual stress after redistribution.
关键词： substrate preheating,?nite element analysis,thermodynamic behavior,selective laser melting,scanning strategy,24CrNiMo alloy steel