Composition and phases in laser welded Al-Cu joints by synchrotron x-ray microdiffraction

摘要： This paper presents the characterization of the intermetallic phases of laser-welded Al-Cu joints by synchrotron trough-the-substrate microdiffraction combined with SEM/EDX and etched/non-etched optical micrographs. Transmission microdiffraction offers the spatial resolution and beam flux necessary to study the intermetallic phases, which in conjunction with the excellent contrast of etched micrographs, rendered possible the phase identification. It was found that the major phases are Al2Cu (θ), Al4Cu9 (γ1) and AlCu (η2) were formed. The Al3Cu4 (ζ1) and δ phases where formed in less amount and found to be the primary cause for cracks inside the weld seam and therefore for the failure of the joint.