摘要： Lead sulfide nanoparticles (PbS NPs) are used in the short wavelength infrared (SWIR) photodetectors because of their excellent photosensitivity, bandgap tunability, and solution processability. It has been a challenge to synthesize high quality PbS NPs with an absorption peak beyond 2000 nm. In this work, using PbS seed crystals with an absorption peak at 1960 nm, we report a successful synthesis of very large mono-dispersed PbS NPs having a diameter up to 16 nm by multiple injections. The resulting NPs have an absorption peak over 2500 nm with a small full-width-at-half-maximum (FWHM) of 24 meV. To demonstrate the applications of such large QDs, broadband heterojunction photodetectors are fabricated with the large PbS QDs of an absorption peak at 2100 nm. The resulting devices have an EQE of 25% (over 50% IQE) at 2100 nm corresponding to a responsivity of 0.385 A/W, and an EQE ~60% in the visible range.