摘要： In this study, carbon quantum dots (CQDs) were used to decorate a TiO2/g-C3N4 (TCN) film electrode. The morphological, optical, and electrochemical properties of the TiO2/g-C3N4/CQDs nanorod arrays (TCNC NRAs) film were investigated using transmission electron microscopy (TEM), scanning electron microscopy (SEM), UV-vis diffuse reflectance spectroscopy (DRS), photoluminescence (PL), and electro-impedance spectroscopy (EIS). The improved optical properties, photoelectrochemical chemical properties and photoelectrocatalytic (PEC) performance of photoanode can be observed by doping CQDs onto the TCN NRAs film. Compared with TiO2 NRAs and TCN NRAs, the narrower band gap of 2.47 eV and longer lifetime of photoinduced electron-hole pairs were observed in the TCNC NRAs. Under visible light irradiation and a bias voltage of 1.2 V, the photocurrent density and 1,4-dioxane (1,4-D) removal rate of PEC process with TCNC NRAs electrode reached 0.16 mA/cm2 and 77.9%, respectively, which was 2.5 times and 1.5 times of that with TCN NRAs electrode. TCNC NRAs electrode could keep >75% of the 1,4-D removal rate during five cycles tests. High PEC performance with TCNC NRAs electrode could be attributed to the enhanced charge separation and the change of electron transfer mechanism from typical heterojunction to Z-scheme, which may increase the active species production and change the dominant reactive species from O2?- to ?OH. Our experimental results should be useful for studying the degradation of 1,4-D and developing efficient PEC materials.